LSCB-7 Methanol Cracking Catalyst Extrudates

I'm Online Chat Now

LSCB-7 Methanol Cracking Catalyst Extrudates

LSCB-7 Methanol Cracking Catalyst Extrudates
LSCB-7 Methanol Cracking Catalyst Extrudates

Large Image :  LSCB-7 Methanol Cracking Catalyst Extrudates

Product Details:
Place of Origin: china
Brand Name: QD
Certification: ISO9001:2015
Model Number: catalyst
Payment & Shipping Terms:
Minimum Order Quantity: 1 kg
Price: USD3000-30000 /Ton
Packaging Details: 25kg/bags or 500kg/bags and carbon
Delivery Time: 5-8days
Payment Terms: T/T, L/C
Supply Ability: 1000Ton per month

LSCB-7 Methanol Cracking Catalyst Extrudates

Description
Shape: Black Extrude CuO (Wt%): ≥65.0
ZnO (Wt%): 8 AL2O3 (Wt%): 8
High Light:

Catalyst Extrudates

,

Methanol Cracking Catalyst

LSCB-7methanol cracking(reforming) catalyst

 

LSCB-7 catalyst is used in methanol cracking to H2 reaction or methanol with water reforming to H2.

The reaction equation is CH2OH → CO+2H2 CH2OH+H2O→ CO2+3H2.

1Activity: in the condition of laboratory, 120ml reduced state catalyst worked in the 1.2h-1 space velocity;

the methanol conversion is showed in the table.

Temperature Methanol conversion
230 ≥75%
250 ≥ 95%

2. Heat up and reduce progress. Because it is hard to control the temperature,

catalyst is usually reduced below 0.5 Mpa.

3. Catalyst normal usage and protection way.

3.1 Fresh reduced catalyst should work in underload condition for several days in order to make the catalyst

activity and service life stabilization.

3.1.2 Fresh reduced catalyst should try its best to work in low temperature on the promise that the catalyst

can satisfy production requirement.

3.1.3 Refining methanol of raw material. Removing the impurity from methanol, especially sulphide and chloride,

can longer catalysts’ service life.(in the condition of S reaching in 0.25 PPM, or CL reaching 0.3PPM,

catalyst activity can cut down 50%)

3.1.4 Catalyst service life mainly depends on whether catalysts suffer from excess-temperature or local over-heating.

Avoiding these also can longer catalyst service life.

3.1.5 Many times Start-up and shutdown will also influence catalyst’s service life. So try to avoid it.

Physical property

Size Ф5×5mm black extrude
Bulk density ≤1.3kg/cm3
Crushing strength ≥80N/cm

Chemical property

CuO (Wt%) ≥65.0
ZnO (Wt%) ≥8.0
AL2O3 (Wt%) ≥8.0
Other promoter (Wt%) ≥2.0
Loss on ignition (540℃/hr) ≤13.0